美国原装进口HARRIS银焊条简介如下：哈利斯磷铜钎料型号AWS A5.8Ag%Cu%P%其他固相线液相线流动性°F°C°F°CBlockade®BCuP-90BAL6.5Si0.01-0.4011786371247674N/AFlash® (LCuP-8)091.98.1131071013407278Stay-Silv® 0HHP092.497.51131071014317696.5Harris 0HP (LCuP-7)BCuP-2092.67.4131071014457856Harris 0BCuP-2092.97.1131071014758025Harris LCuP-6092.56.5131071015498433Stay-Silv® 2HP290.67.4119064314057635Stay-Silv® 2BCuP-62917119064314507884Stay-Silv® 2LP291.46.6119064315008163Stay-Silv® 5HP588.66.4119064314457854Stay-Silv® 5BCuP-35896119064315008163Stay-Silv® 5LP589.35.7119064315358352Dynaflow®687.96.1119064314657963Stay-Silv® 6HPBCuP-4686.87.2119064313357247Stay-Silv® 6687.56.5119064314257745Stay-Silv® 6LP687.86.2119064314557914Stay-Silv® 15BCuP-515805119064314808043Stay-Silv® 181875.46.6119064312206607哈利斯银基钎料型号AWS A5.8Ag%Cu%Zn%Ni%Sn%其他固相线液相线流动性°F°C°F°CSafety-Silv® 252543302127068814357795Safety-Silv® 30BAg-20303832125067714107666Safety-Silv® 35BAg-35353233125067713507325Safety-Silv® 38TBAg-343832282122066013257187Safety-Silv® 404030.529.5125066013507325Safety-Silv® 40Ni2BAg-4403028122067714357794.5Safety-Silv®40TBAg-284030282122066013107106.5Safety-Silv® 45BAg-5453025122566313707436.5Safety-Silv® 45TBAg-364527253119664612656857Safety-Silv® 49NBAg-224916234.5Mn7.5126068012906998Safety-Silv® 50BAg-6503416127068814257745.5Safety-Silv® 50NBAg-24502028122066013057077Safety-Silv® 54BAg-1354405113407261575857Safety-Silv® 56BAg-75622175114561812056528Safety-Silv® 56NBAg-13A56402142077116408935Safety-Silv® 60TBAg-1860Rem10111560213257184.5Safety-Silv® 63TBag-216328.52.56127569114758025Safety-Silv® 72BAg-872281435779143577910Safety-Silv®72VBVAg-8722814357791435779Safety-Silv® 99.9(Pure Silver纯银)BVAg-099.917619611761961商品記號內容形狀規格尺寸(mm)包裝方式Harris 00%扁型1.3 mm x 3.2 mm x 500 mm L.透明管包裝/每1公斤Harris 00%圓型Φ 2.4 mm x 500 mm L.透明管包裝/每1公斤Harris 00%扁型1.3 mm x 3.2 mm x 500 mm L.紙盒包裝/每11.34公斤Harris 00%圓型Φ 2.4 mm x 500 mm L.紙盒包裝/每11.34公斤Stay-Silv 22%扁型1.3 mm x 3.2 mm x 500 mm L.透明管包裝/每1公斤Stay-Silv 22%圓型Φ 2.4 mm x 500 mm L.透明管包裝/每1公斤Stay-Silv 22%扁型1.3 mm x 3.2 mm x 500 mm L.紙盒包裝/每11.34公斤Stay-Silv 22%圓型Φ 2.4 mm x 500 mm L.紙盒包裝/每11.34公斤Stay-Silv 55%扁型1.3 mm x 3.2 mm x 500 mm L.透明管包裝/每1公斤Stay-Silv 55%圓型Φ 2.4 mm x 500 mm L.透明管包裝/每1公斤Stay-Silv 55%扁型1.3 mm x 3.2 mm x 500 mm L.紙盒包裝/每11.34公斤Stay-Silv 55%圓型Φ 2.4 mm x 500 mm L.紙盒包裝/每11.34公斤Stay-Silv 1515%扁型1.3 mm x 3.2 mm x 500 mm L.透明管包裝/每1公斤Stay-Silv 1515%圓型Φ 2.4 mm x 500 mm L.透明管包裝/每1公斤Stay-Silv 1515%扁型1.3 mm x 3.2 mm x 500 mm L.紙盒包裝/每11.34公斤Stay-Silv 1515%圓型Φ 2.4 mm x 500 mm L.紙盒包裝/每11.34公斤

焊条典型性能纤维素焊条品名AWS型号特 性 与 用 途PIPEMASTER PRO60E6010纤维素焊条，可用于X42到X65大直径管线焊接，也可用于X52-X70钢管的根焊。PIPEMASTER 70E7010-P1纤维素焊条，可用于X52到X65钢大直径管线焊接。PIPEMASTER 80E8010-P1纤维素焊条，可用于X56到X70钢大直径管线焊接。PIPEMASTER 90E9010-G纤维素焊条，可用于X65到X80钢大直径管线焊接。低合金钢焊条品名AWS型号特 性 与 用 途HOBART 7018XLME7018-1 H4R难吸潮超低氢焊条，低温韧性好，可用于锅炉、压力容器等焊接。HOBART 7016E7016 H4低氢型焊条全位置焊接性能好，用于X80钢管的根焊（上坡焊）。HOBART 718XCE7018-1 H4R难吸潮超低氢焊条，低温韧性好，焊接重要结构。HOBART 7018A1E7018A1 H4R用于焊接0.5% Mo钢,也可用于管线焊接。HOBART 8018B2E8018-B2 H4R低氢耐热钢焊条，焊接1.25Cr-0.5Mo钢。HOBART 8018B2LE8018-B2LH4R焊碳比8018B2低,韧性好，焊接1.25Cr-0.5Mo钢,可降低预热温度。HOBART 8018C1E8018-C1 H4R用于焊接低温工作的储气罐等。HOBART 8018C2E8018-C2 H4R用于焊接低温工作的3.5Ni钢制储气罐。HOBART 8018C3E8018-C3 H4R用于焊接60公斤级高强钢及1%Ni钢。HOBART 9018B3E9018-B3 H4R低氢耐热钢焊条，焊接2.25Cr-1Mo钢。HOBART 9018B3LE9018-B3LH4R焊碳比9018B3低,抗裂性好。HOBART 9018ME9018-M H4R焊接HY80、HY90、T-1等高强钢。HOBART 10018D2E10018-D2 H4R焊接Mn-Mo型钢，压力容器部件或铸钢件。HOBART 11018ME11018-M H4R焊接HY80、HY90、HY100及低合金高强钢。HOBART 12018ME12018-M H4R焊接相应强度的低合金钢结构。气保护药芯焊丝品名AWS型号特 性 与 用 途FabCO 85E70T-J5/-5MJ碱性渣系焊丝，焊接低合金高强钢及某些中碳钢结构。FabCO 115E110T5-K4焊接如Hy100高强钢制成的矿山采挖设备。FabCO RXRE70T-1适合于焊接表面有氧化皮、油污等的代碳钢结构。FabCO TR-70E70T-1/T-9低烟尘、飞溅少、焊接低碳钢及低合金钢。FabCO 86RE70C-6MH4金属粉芯焊丝，有较高的熔敷率、飞溅少。Excel-Arc71E71T-1/-1M熔深大，全位置焊性能好，飞溅小，用于碳钢及低合金钢焊接。Excel-Arc71E71T-9/-9M熔深大，全位置焊性能好，飞溅小，用于碳钢及低合金钢焊接。Formula XL-550E71T-1H8/-12J焊接船舶、贮罐、推土设备及管道。Formula XL-8Ni1E81T1-Ni1 H8MJ焊接船舶、贮罐、推土设备及管道。FabCO 81K2-CE81T1-K2CJ H8力学性能好，扩散氢含量低，用于焊接船舶、海洋平台等。FabCO 91K2-CE91T1-K2在抗拉强度620-770MPa范围内有良好的冲击韧性，焊接如Hy100等高强钢。自保护药芯焊丝品名AWS型号特 性 与 用 途Fabshield 4E70T-4有强的脱硫能力和抗裂性，焊接低碳钢和中碳钢。Fabshield 7027E70T-7具有优良的电弧特性及高的熔敷速度，适合于大电流，焊接钢结构。Fabshield 71K6E71T8-K6J焊接X42-X70管线及海洋平台等钢结构。Fabshield X70E71T8-GJ焊接X42-X70管线及海洋平台等钢结构。Fabshield 81N1E71T8-Ni1J焊接X42-X70管线及海洋工程。Fabshield 81N2E81T8-Ni2焊接X8管线及海洋平台、储罐等。Fabshield X80E81T8-Ni2J焊接X8管线及各种钢结构。Fabshield XLR-8E71T-8JD H8对焊接热输入范围适应性好，可用大电流进行立向上焊。符合AWSA5.20-2005标准中新的D类要求.用于钢结构焊接.Fabshield 21BE71T-11全位置焊接性好,特别适宜焊薄的碳钢及镀锌钢板等轻型结构。Fabshield 23E71T-GS适用单道填充几盖面焊,焊镀锌板等钢结构碳钢、低合金与金属粉药芯焊丝金属粉药芯焊丝品名类别AWS型号熔敷金属化学成分（%）熔敷金属力学性能特性与用途CMnSiCrNiσ0.2(MPa)δb(MPa)δ(%)金属粉型药芯焊丝Metalloy 71E70C-6M H40.051.340.7547655927几乎无飞溅、无渣，溶敷率高，扩散氢含量低，当采用短路或脉冲过渡时，可全位置焊Metalloy 76E70C-6M H40.061.640.7555962827熔敷金属锰含量高、强度高，其它同M.71，可焊碳钢及低合金钢，供X70钢管半自动和自动焊用Metalloy VANTAGEE70C-6M H40.051.380.650.4055262225有较高的强度和韧性，且飞溅及渣极少可降低清理成本Metalloy 80N1E80C-Ni10.041.140.400.9753562126低温韧性好，用于焊接Ni-Mo钢，如0.5Ni-0.25Mo等，也可用于X70钢管的焊接Metalloy 80N2E80C-Ni20.041.090.342.2653162126低温韧性好，用于焊接海洋平台、船舶等重要结构Metalloy 80D2E90C-D20.081.940.6672077122相当于ER80S-D2实芯焊丝，但焊接工艺性能及抗吸潮性更好、焊高强钢Metalloy 80B2E80C-B20.070.820.291.3648057523焊接2.25Cr-1Mo耐热钢Metalloy 90B3E90C-B30.070.700.352.3055465420焊接2.25Cr-1Mo耐热钢Metalloy 80WE80C-G0.041.190.630.550.6164270424焊接高强度、低合金耐候钢Metalloy 90E90C-G0.051.320.331.8963169625用于焊接对低温韧性有较高要求的高强钢，如海洋平台、船舶等Metalloy 100E100C-G0.071.500.381.5871278121焊高强钢，X100管线钢的自动焊或半自动焊，当要求高匹配时，也可焊X80钢Metalloy 110E110C-G0.071.630.480.212.2275382722焊高强钢，如T-1、HY80、HY100等碳钢及低合金钢药芯焊丝品名类别AWS型号熔敷金属化学成分（%）熔敷金属力学性能性能及用途CMnSiCrNiσ0.2(MPa)δb(MPa)δ(%)碳钢及低合金钢药芯焊丝Triple-7E71T-1H80.031.010.3450457327用于碳钢及高强钢的半自动和自动焊，渣快疑TM711E71T-1H80.080.980.5253861429用于碳钢半自动焊，立仰焊性好，深坡口内脱渣好，用于船舶修造及钢结构焊接Triple-8E71T1-10.071.250.5353860026低温韧性好，飞溅小，可全位置焊TM910E71T1-1M0.060.820.4050556826既适用大热输入及缓冷，也可用于小热输入及快冷，工艺性能与力学性能均优TM-811A1E81T1-A10.100.990.4058769022焊接0.5%Mo耐热钢TM-811B2E81T1-B20.060.800.331.2960068321焊接1.25Cr-0.5Mo耐热钢TM-911B3E91T1-B30.080.690.292.3366275218焊接2.25Cr-1Mo耐热钢TM-B9E91T1-Ni20.120.600.159.077286915焊接高温高压条件下工作的T/P91耐热钢TM-811N1E81T1-Ni10.080.960.420.9851160026用于石化工业中要求低温韧性好的钢结构TM-811N2E81T1-Ni20.080.820.312.5949058024扩散氢低及韧性好，焊接船舶、海洋平台TM-105D2E100T5_D20.112.000.5566976624碱性渣，焊接低温韧性好的70Kgf级高强钢TM-991K2E91T1K2/K2M0.051.140.191.9255263527具有良好的低温韧性的高强的焊丝，好的全位置焊接性，可焊Hy-80等高强钢TM-105K3E100T2-K30.071.440.481.8466978024碱性渣，抗裂性好，焊接80kgf级高强钢TM-110K3-ME111T1-K3MJH80.051.460.320.032.0871875921强度、韧性高，含氢量低，焊高强钢TM-115E110T5-K30.071.880.562.0471182123焊接80kgf级调质钢，如A514517钢TM-125K4R120T5-K40.101.880.420.522.1381491820具有高的低温韧性，焊接低合金高强钢不锈钢药芯焊丝气保护焊丝品名类别AWS型号熔敷金属化学成分（%）熔敷金属力学性能特性及用途CMnSiCrNiσ0.2(MPa)δb(MPa)δ(%)气保护焊丝In-Flux308T1E308T1-4/-10.061.280.4920.1410.1744262839焊接18-8型(304)铬镍不锈钢In-Flux308LT1E308LT1-4/-10.031.100.7019.609.5042158743焊接超低碳18-8型(304L)铬镍不锈钢In-Flux309LT1E309LT1-4/-10.031.330.6023.1013.0046261437焊接超低碳18-8型(309L)不锈钢及异种钢In-Flux309MoLT1E309MoLT1-4/-10.031.200.6023.0012.5041462434用于碳钢与316L不锈钢的异种钢焊接In-Flux316LT1E316LT1-4/-10.031.330.5818.8013.1043558733焊接超低碳18-12-2型(316L)铬镍不锈钢In-Flux347T1E317LT10.051.200.6019.509.5040058735焊接18-8含钛(321)、含铌(347)不锈钢In-Flux410NiMoT1E410NiMoT1-4/-10.030.300.3811.504.301000111720焊接CA-6NM不锈钢铸件及409、410、410及405等铬不锈钢In-Flux2209T1E2209T1-4/-10.041.710.7123.619.1363580724焊接2205双相不锈钢自保护焊丝品名类别AWS型号熔敷金属化学成分（%）熔敷金属力学性能特性及用途CMnSiCrNiσ0.2(MPa)δb(MPa)δ(%)自保护焊丝In-Flux308L-OE308LT0-30.031.100.4420.209.8048364940焊接304L不锈钢，也可作堆焊过渡层In-Flux309L-OE309LT0-30.031.730.5823.1012.9048362840焊接304L、309L不锈钢及异种钢In-Flux316L-OE316LT0-30.022.120.4419.1011.9046961440焊接316、316L不锈钢In-Flux410NiMo-OE410NimOT0-30.030.440.3112.104.6076690421焊接CA-6NM及420马氏体不锈钢，焊410钢比410型填充金属抗裂性好赫伯特堆焊焊材堆焊焊条药芯焊丝品名类别熔敷金属化学成分（%）熔敷金属力学性能特性及用途CMnSiCrNiσ0.2(MPa)δb(MPa)δ(%)硬度(HRC一层)硬度(HRC三层)堆焊焊条Hardalloy 1180.8016.50.505.00.305388765018-2250-55抗冲击磨损性**，抗磨擦磨损性好，焊补Mn13型高锰钢Chrome-Mang0.4014.50.6014.01.06498974050-55抗冲击磨损性**，抗磨擦磨损性好，焊补Mn13型高锰钢Hardalloy 580.061.200.705.5045-5555-60抗冲击磨损性好，抗粘附磨损性好，既可修补，也可堆焊Hardalloy 1403.000.402.030.05357在650℃时仍维持较高耐磨性，可在奥氏体钢、锰钢表面堆焊Hardalloy 1481.800.601.8030.03.03643适用于金属对金属间磨损，高温时仍保持较高硬度Hardalloy 40TiC3.001.100.808.203950堆焊金属含有碳化钛提高耐磨性，适于焊中等冲击而磨损严重的工件Hardalloy 610.800.500.704.053-5557-63成分与高速工具钢相似，适于高温下金属间磨损件堆焊Hardalloy 1-C2.500.501.030.049-5949-59钴基合金焊条750℃高温下仍有较高的耐磨性Hardalloy 6-C1.001.001.0030.1,&, lt;, /TD>35-4535-45钴基合金焊条750℃高温下仍有较高的耐磨性，抗裂性比1-C好McKAY C0.030.600.4015.5余量30-40钴基合金焊条750℃高温下仍有较高的耐磨性品名类别熔敷金属化学成分（%）熔敷金属力学性能特性及用途CMnSiCrNiσ0.2(MPa),δb(MPa)δ(%)硬度(HRC一层)硬度(HRC三层)药芯焊丝Tube-Alloy 218-01.015.00.403.10.415-2250-55为加工硬化型奥氏体锰钢，堆焊焊层韧性高，在高冲击下快速实现加工硬化，也可用于锰钢之间的连接焊Tube-Alloy AP-00.4216.50.3013.018-2450-55基本与Tube-Alloy218-0相同，但韧性更好Tube-Alloy 240-03.21.801.9015.54052为碳化铬型合金，堆焊层韧性好Tube-Alloy 255-04.500.900.5026.55458为碳化铬型合金，用于磨料磨损及中等冲击处焊接，也在可在较高温度下(675℃)工作Tube-Alloy 255-04.500.900.5026.55458为碳化铬型合金，用于磨料磨损及中等冲击场合，也可在较高温度(675℃)下工作Verti Wear 6000.400.750.606.505257为马氏体型合金，用于中度磨料磨损及中到高度冲击场合Tube-Alloy 2582.101.301.807.06048为含大量TiC的马氏体型合金，对高应力磨料磨损特别好，也有好的高温硬度(U.S.＊＊No.3231709)Tube-Alloy A43-O5.500.21.022.05862为含大量Cr,Nb碳化物的合金，对高及低应力磨料磨损特别好，也可用于要求高温(675℃)耐磨的场合Tube-Alloy A45-O5.500.21.021.06064在奥氏体中含有大的碳化铬及细小的碳化铌及合金碳化物，用于高温下并伴有小的冲击的低及高应力磨损场合，如高炉料钟Tube-Alloy 242-O0.251.300.704.03642为马氏体型合金，耐金属与金属间磨损, >药芯焊丝品名类别熔敷金属化学成分（%）熔敷金属力学性能特性及用途CMnSiCrNiσ0.2(MPa)δb(MPa)δ(%)硬度(HRC一层)硬度(HRC三层)药芯焊丝Tube-Alloy 218-01.015.00.403.10.415-2250-55为加工硬化型奥氏体锰钢，堆焊焊层韧性高，在高冲击下快速实现加工硬化，也可用于锰钢之间的连接焊Tube-Alloy AP-00.4216.50.3013.018-2450-55基本与Tube-Alloy218-0相同，但韧性更好Tube-Alloy 240-03.21.801.9015.54052为碳化铬型合金，堆焊层韧性好Tube-Alloy 255-04.500.900.5026.55458为碳化铬型合金，用于磨料磨损及中等冲击处焊接，也在可在较高温度下(675℃)工作Tube-Alloy 255-04.500.900.5026.55458为碳化铬型合金，用于磨料磨损及中等冲击场合，也可在较高温度(675℃)下工作Verti Wear 6000.400.750.606.505257为马氏体型合金，用于中度磨料磨损及中到高度冲击场合Tube-Alloy 2582.101.301.807.06048为含大量TiC的马氏体型合金，对高应力磨料磨损特别好，也有好的高温硬度(U.S.＊＊No.3231709)Tube-Alloy A43-O5.500.21.022.05862为含大量Cr,Nb碳化物的合金，对高及低应力磨料磨损特别好，也可用于要求高温(675℃)耐磨的场合Tube-Alloy A45-O5.500.21.021.06064在奥氏体中含有大的碳化铬及细小的碳化铌及合金碳化物，用于高温下并伴有小的冲击的低及高应力磨损场合，如高炉料钟Tube-Alloy 242-O0.251.300.704.03642为马氏体型合金，耐金属与金属间磨损

ARCOSAWSMilitary应用382ERNiCr-3EN/RN82合金600 601 800自身的焊接以及不锈钢和碳钢之间的焊接352ERNiCrFe-7N/A焊接ASTM B163 166 167和168标准内的镍铬铁合金392ERNiCrFe-6EN6a/RN6A镍铬铁与钢复合，钢和不锈钢同镍基合金的焊接617ERNiCrCoMo-1N/A焊接镍铬钴钼合金以及焊接各种不同的高温合金625ERNiCrMo-3EN/RN625用于镍合金，碳钢，不锈钢和低合金钢各种类型的焊接，*主要用于625 601 802合金和9%镍合金的焊接651ERNi-CiN/A工业纯镍，用于焊接可锻铸铁和灰口铸铁813ERCuNiEN/RN67用于70/360 80/20和90/10铜镍合金的焊接816ERNICu-7EN/RN60焊接镍钢合金B127 163 164 165861ERNi-1EN/RN61用于纯镍锻件和铸件的焊接,如ASTM160 161 162 163标准内的合金2216ERNiFeMn-CiN/A用于结节铸铁,球墨铸铁,可锻铸铁和灰口铸铁自身的焊接或者同不锈钢,碳钢,低合金钢和各种镍合金的焊接C-276ERNiCrMo-4N/A用于镍铬钼合金自身的焊接,钢及大多数其它镍基合金的焊接C22ERNiCrMo-11N/A镍铬钼合金自身的焊接,钢和其它镍基合金的焊接和钢的堆焊Alloy59ERNiCrMo-13N/A用于焊接低碳镍铬钼合金焊条1N12ENICrMo-31N12用于焊接镍铬钼合金,如625 800 801 825 6008N12ENICrFe-38N12H用于镍铬钼合金自身的焊接,钢及碳钢的焊接4N1AENICrFe-24N1A用于奥氏体钢,铁素体钢和高镍合金各种类型的焊接,也可用于9%镍合金的焊接9N10ENiCu-79N10主要用于镍钢合金自身的焊接以及它们和钢之间的焊接352ENICrFe-7N/A焊接镍铬铁合金690(UNS N06690)自身C-276ENICrMo-4N/A焊接C-276合金自身以及大多数其它镍基合金617ENICrCoMo-1N/A焊接镍铬钴钼合金以及焊接各种不同的高温合金

美国安科代理   现货供应ARNCO焊丝的常见规格有：100XT、150XT、200XT 300XT300XT和200XT都会产生裂纹（无论细微裂纹或应力裂纹），而若操作合理，100XT和150XT不会产生可见的裂纹。如果加焊耐磨带的母材金属类型不同，各种焊丝的预热温度也会不同。针对某种特定外径或者多类外径尺寸，现在预热温度的规定较以前更加详细焊接安科100XT、150XT或300XT耐磨带时，必须为焊弧提供保护气体。安科根据经验了解到，焊接时可使用100%的纯二氧化碳，或者使用氩和二氧化碳混合气体。指定的氩/二氧化碳气体混合物为；a) 82%氩/18%二氧化碳，或者b) 80%氩/20%二氧化碳水，或者c）75%氩/25%二氧化碳。不应使用其它氩和二氧化碳混合比率，因为它们可能对焊接产生负面影响。必须控制所有气体的调节径流，使向焊孤区输送的气体流量保持在30至35 CFH (14-16.5 LPM)。有风条件下，在管具场地或钻机位置使用移动式耐磨带焊接设备时，应严格注意保护焊枪箱内喷嘴附近的气流，防止其在焊接时被吹离焊孤。安科200XT焊丝是一种自保护焊丝，因此它不需要保护气 随着钻井技术的进步，对钻具街头耐磨性的要求越来越高，必须使用高性能的耐磨材料，才能适应不同类型钻井的需求。上世纪30年代，采用钨钴系列硬质合金耐磨带，如碳化钨[2]  等。碳化钨耐磨带在裸眼中能较好地保护钻杆，但堆层组织中高硬度的碳化钨颗粒对套管产生较大的磨损，影响钻井工程进度和经济效益。为此，在国际钻井工程招标中或国内较深井钻井中，碳化钨硬质合金接头耐磨带都被明令禁用。上世纪90年代，一种平衡磨损思路被提出，它所坚持的理念是，尽量减小套管的被动磨损，同时允许钻杆接头适度磨损。钻杆耐磨带焊丝选用硬度大于HRC50，耐磨性较好，磨损率较小。现场应用表明，在减小钻杆磨损的前提下，能有效地降低套管的磨损。